Low-temperature Heat Capacities and Thermodynamic Properties of Hydrated Sodium Cupric Arsenate [ NaCuAsO4·1.5H2O(s)]

Low-temperature heat capacities of the solid compound NaCuAsO4 · 1.5H2O(s) were measured using a precision automated adiabatic calorimeter over a temperature range of T = 78 K to T = 390 K. A dehydration process occurred in the temperature range of T = 368-374 K. The peak temperature of the dehydration was observed to be TD = (371.828±0.146) K by means of the heat-capacity measurement. The molar enthalpy and entropy of the dehyperimental values of heat capacities for the solid(Ⅰ) and the solid-liquid mixture(Ⅱ) were respectively fitted to two polynomial equations by the least square method. The smoothed values of the molar heat capacities and the fundamental thermodynamic functions of the sample relative to the standard reference temperature 298.15 K were tabulated at an interval of 5 K.     

酞侧基聚芳醚砜和聚芳醚酮共混物的高温流变行为

用锥板粘度计测试了酞侧基聚芳醚砜（ＰＥＳ－Ｃ）和酞侧基聚芳醚酮（ＰＥＫ－Ｃ）及其共混物的熔体流变行为．试样的流动活化能分别为１４５、１３３和１１２ＫＪ／ｍｏｌ．共混物的熔体粘度显著低于ＰＥＳ－Ｃ和ＰＥＫ－Ｃ粘度的对数加和值．并证明试样的熔体流动性和加工稳定性都已达到注射成型工艺的要求．     

孔壁部分有序化的介孔二氧化硅材料的合成与表征

采用一种“改进的二次晶化”的方法处理介孔二氧化硅SBA-15. 用X射线衍射(XRD)、 透射电镜(TEM)、 电子衍射(ED)、 红外光谱(FTIR)以及固体核磁共振(NMR)等多种技术对样品进行了表征.　结果表明， 在所得样品的孔壁中, 原子的排列方式与普通介孔二氧化硅材料的孔壁不同， 显示一定程度的有序性. 同时, 高度有序的介孔结构得到很好的保持, 且样品的水热稳定性大幅度提高.     

Pt3Co核-Pt壳型纳米粒子的制备及磁性

Pt₃Co alloy nanoparticles were prepared by the reduction of H₂PtCl₆ and Co(OOCCH₃)₂ using NaBH₄ as a reducing agent. The Pt₃Co core-Pt shell nanoparticles (Pt₃Co@Pt) were synthesized using hydrogen absorption reduction and characterized by plasma-atomic emission spectrometry (ICP), transmission electron microscopy (TEM), X-ray diffraction (XRD) and SQUID magnetometer. The results show that average size of Pt₃Co@Pt nanoparticles is 3.6 nm with a standard deviation of 0.9 nm. Heating Pt₃Co nanoparticles in air at 700 ℃ for 1 h, Co in Pt₃Co nanoparticles was oxidized to Co₃O₄ and CoO; while no oxidation tendency was detected for Pt₃Co@Pt nanoparticles. The crystallize structure of Pt₃Co@Pt changed from the face centered cube (fcc) to the face centered tetragonal (fct) after the heating treatment. The coercivity of the heated Pt₃Co@Pt reached to 276 Oe at room temperature.     

新的脉冲进样AAS法测定“麻杏石甘汤”中的微量金属元素

本文研制了一种新的脉冲进样装置，用于火娄原子吸收分光光度法测定中药煎剂中的Ｃａ，Ｍｇ，Ｆｅ，Ｍｎ，Ｚｎ五种金属元素含量，实验表明，利用此种装置可以同时获得两种进样方式的分析结果，线性范围比常规法宽两倍，耗样量，精密度及分析速度均优于常规法。     

稀土高氯酸盐-谷氨酸配合物[Pr2(L-α-Glu)2(ClO4)(H2O)7](ClO4)3•4H2O的低温热容和热化学研究

合成了一种稀土高氯酸盐-谷氨酸配合物. 经TG/DTG、化学和元素分析、FTIR及与相关文献对比, 确定其组成为[Pr₂(L-α-Glu)₂(ClO₄)(H₂O)₇](ClO₄)₃•4H₂O, 纯度为99.0%以上. 利用显微熔点仪分析发现其没有熔点. 在78～370 K温区, 用精密绝热量热仪测量其低温热容, 在285～306 K温区发现一明显吸热峰, 归结为固-固相变过程. 通过相变温区三次重复热容测量, 得到相变温度T_tr、相变焓Δ_trH_m和相变熵Δ_trS_m分别为(297.158±0.280) K, (12.338±0.016) kJ•mol^－1和(41.520±0.156) J•K^－1•mol^－1. 用最小二乘法将非相变温区的热容对温度进行拟合, 得到了热容随温度变化的两个多项式方程. 用此方程进行数值积分, 得到每隔5 K的舒平热容值和相对于273.15 K的热力学函数值. 根据TG/DTG结果, 推测了该配合物的热分解机理. 依据Hess定律, 选择1 mol•dm^－3盐酸为量热溶剂, 利用等温环境溶解-反应量热计, 测定了该配合物的标准摩尔生成焓为: Δ_fH_m⁰＝－(7223.1±2.4) kJ•mol^－1.     

聚醚砜流变性能的研究

用锥板流变仪测试了分子量不同的国产聚醚砜（ＰＥＳ）样品的流变性能。结果表明ＰＥＳ具有剪切变稀的特性，所得的粘流活化能与文献报道的ＩＣＩ产品值相近。根据求得的零剪切粘度（ηｏ）与分子量的关系推断样品的分子量已经接按临界分子量（Ｍｃ），并利用转换因子αＩ＝ηｏＴ／ηｏ（ＴＲ）绘制了样品的叠合曲线，得到较好的叠加效果，同时还求得了ＷＬＦ方程的两个经验常数Ｃ１和Ｃ２的数值。     

HDDR过程中三元和多元Nd-Fe-B合金磁畴结构的MFM研究

用磁力显微镜研究了三元Nd-Fe-B合金在HDDR过程的不同阶段(铸态、不充分吸氢歧化、充分吸氢歧化和脱氢再复合)的破畴结构。在铸态样品表面清楚地观察到了易磁化轴互相垂直的柱状晶表面的两类磁畴图型。当样品不充分吸氢歧化和充分吸氢歧化时，破畴结构明显发生变化，反映了Nd-Fe-B的分解产物NdH2，α-Fe和Fe2B及其微晶结构的变化。脱氢再复合后形成的微晶的磁畴结构则表明样品保留了铸态样品柱状晶的构型。此外，还对比研究了多元Nd-Fe-B合金在HDDR过程中的磁畴结构，并根据微磁结构分析，指出过量的Ga元素添加可抑制Nd2(Fe，M)14B相的吸氢歧化，从而导致相应HDDR粘结磁体性能降低。     

杯芳烃修饰玻碳电极吸附溶出伏安法测定微量铅

研究了以杯芳烃衍生物修饰玻碳电极,以其吸附溶出伏安法测定微量铅。对富集时间、铅的浓度、支持电解质、样品溶液pH值及部分离子干扰等进行了实验。实验发现以氢氧化钠溶液处理修饰电极可提高测定灵敏度,经过优化处理后,线性范围和检出限分别为5.0×10-7～1.0×10-5mol/L和1.0×10-8mol/L。应用本法对合成水样进行了测定,结果满意。本文还对吸附溶出机理进行了讨论。     

D-甘露醇与D-山梨醇在氯化钠水溶液中的稀释焓

应用等温流动微量热法测定了298.15 K时互为旋光异构体的D-甘露醇与D-山梨醇在不同浓度的氯化钠水溶液中的稀释焓, 利用 McMillan-Mayer 理论计算了D-甘露醇与D-山梨醇在不同浓度的氯化钠水溶液中的焓对相互作用系数. 结果表明, D-甘露醇和D-山梨醇在氯化钠水溶液中的焓对相互作用系数h2均为正值, h2的值随着氯化钠浓度的增加皆逐渐增大, 但D-山梨醇的焓对相互作用系数h2增大的速率[dh2 /dm(NaCl)]比 D-甘露醇的要大. 根据两多元醇分子构象结构的差异， 溶质-溶质相互作用和溶质-溶剂相互作用对结果进行了解释.